購買設(shè)計請充值后下載，，資源目錄下的文件所見即所得，都可以點開預(yù)覽，，資料完整，充值下載就能得到。。?！咀ⅰ浚篸wg后綴為CAD圖，doc,docx為WORD文檔，【有不明白之處，可咨詢QQ:1304139763】
Journal of Mechanical Science and Technology 24 2010 145 148 DOI 10 1007 s12206 009 1126 5 Optimal injection molding conditions considering the core shift for a plastic battery case with thin and deep walls Dong Gyu Ahn 1 Dae Won Kim 2 and Yeol Ui Yoon 3 1 Department of Mechanical Engineering Chosun University Gwang Ju 501 751 Korea 2 Incheon Service Division KITECH Incheon 406 840 Korea 3 Chun Bok Injection Mold Inc Gwang Ju 1233 12 Korea Manuscript Received April 24 2009 Revised September 21 2009 Accepted October 12 2009 Abstract The objective of this paper is to examine the influence of injection molding parameters on the core shift to obtain the optimal injection molding conditions of a plastic battery case with thin and deep walls using numerical analyses and experiments Unlike conventional injection molding analysis the flexible parts of the mold were represented by 3 D tetrahedron meshes to consider the core shift in the numerical analysis The design of experiments DOE was used to estimate the proper molding conditions that minimize the core shift and a dominant parameter The results of the DOE showed that the dominant parameter is the injection pressure and the core shift de creases when the injection pressure decreases In addition it was shown that the initial mold temperature and the injection time hardly affect the core shift The results of the experiments showed that products without warpage are manufactured when the injection pressure is nearly 32 MPa Comparing the results of the analyses with those of the experiments optimal injection molding conditions were deter mined In addition it was shown that the core shift should be considered to simulate the injection molding process of a plastic battery case with thin and deep walls Keywords Optimal injection molding condition Core shift Thin and deep walls Battery case Design of experiments 1 Introduction One of the recent concerns in the automotive industry is the reduction of overall weight to improve fuel efficiency and re duce a vehicle s environmental impact 1 3 The injection molding process of thinner plastic components allows consid erable weight savings on the automotive a significant reduc tion in production cost and a shorter cycle time 1 Various studies are actively undertaken in an effort to develop the injec tion molding process of thin wall plastic parts 1 High injec tion pressure and high injection speed are necessary to manu facture plastic parts with thin and deep walls 4 However a high injection pressure can give rise to a core shift which is the spatial deviation of the position of the core during injection molding 5 Shepard et al found that the mold design and injection molding conditions strongly affect the core shift of the mold 6 Leo et al reported that the deflection of weak plates in the mold causes variations in the thickness of the product and the over packing of moldings 7 Bakharev et al reported that core shift effects in injection molding can be pre dicted through mold filling simulation coupled with an elastic analysis of the flexible parts of the mold 4 In this paper the influence of injection molding parameters on the core shift in the injection molding of a plastic battery case with thin and deep walls is examined to estimate an op timal injection molding condition The design of experiments is used to estimate a proper molding condition minimizing the core shift as well as to determine a dominant molding pa rameter Several experiments are carried out to obtain an op timal injection pressure Comparing the results of numerical analyses with those of the experiments the optimal injection molding condition is acquired The effects of the core shift on the quality of the product are also discussed 2 Numerical analysis and experiments In order to simulate the core shift and injection molding characteristics a three dimensional injection molding analysis was performed using the commercial code MPI V6 1 Fig 1 illustrates the analysis model The dimensions of the battery case are 164 4 mm W 251 4 mm L 184 0 mm H The maximum and minimum thicknesses of the walls are 2 7 mm and 1 8 mm respectively The depth of the walls is 168 7 mm The runner system consists of a conical sprue with an initial This paper was presented at the ICMDT 2009 Jeju Korea June 2009 This paper was recommended for publication in revised form by Guest Editors Sung Lim Ko Keiichi Watanuki Corresponding author Tel 82 62 230 7043 Fax 82 62 230 7234 E mail address smart mail chosun ac kr KSME Springer 2010 146 D G Ahn et al Journal of Mechanical Science and Technology 24 2010 145 148 Table 1 Parameters and their levels for the DOE Level Parameters 1 2 3 A Initial mold temperature o C 35 0 40 0 45 0 B injection time seconds 1 6 2 2 2 8 C Injection pressure MPa 40 0 35 0 30 0 D Holding time seconds 2 0 3 2 4 4 a b Fig 1 Design of the runner system and core a Design of the runner system and product b Meshes for the flexible parts of the core a b Fig 2 Mold for the manufacture of the plastic battery case a Design of the mold b Manufactured mold diameter of 8 mm and a final diameter of 15 mm circular runners with diameters of 8 mm and pin point gates with diameters of 2 mm In order to consider the core shift phe nomenon in the numerical analysis the flexible parts of the mold and the flow part were represented by 376 674 EA of tetrahedron meshes and 61 098 EA of shell meshes respec tively The injection material was a polypropylene resin The melting temperature of PP was set at 230 o C The design of experiments DOE was used to quantita tively examine the influence of injection molding parameters on the core shift Table 1 shows the injection molding parame ters and their levels for the L 9 3 4 orthogonal array The sig nal to noise S N ratio with the smaller the better characteris tics was calculated to estimate the proper condition for mini mizing the core shift The contribution ratio of each parameter is estimated using Analysis of Variance ANOVA to obtain the dominant parameter affecting the core shift Several experiments were performed using an injection molding machine with 600 tons of clamping force Fig 2 shows the design of the mold as well as the manufactured Table 2 Orthogonal array and results of the numerical analyses Deformation of flexible parts mm of Exp ABCD F1 F2 F3 F4 F5 F6 1 1 1 1 1 0 16 0 11 0 07 0 14 0 08 0 23 2 1 2 2 2 0 18 0 09 0 07 0 14 0 08 0 23 3 1 3 3 3 0 13 0 09 0 05 0 11 0 08 0 16 4 2 1 2 3 0 14 0 10 0 07 0 13 0 08 0 18 5 2 2 3 1 0 12 0 09 0 05 0 11 0 08 0 16 6 2 3 1 2 0 14 0 10 0 07 0 14 0 08 0 21 7 3 1 3 2 0 11 0 09 0 05 0 10 0 08 0 15 8 3 2 1 3 0 17 0 10 0 07 0 14 0 08 0 23 9 3 3 2 1 0 15 0 10 0 07 0 15 0 08 0 22 Fig 3 Results of the numerical analysis Core shift mold for the experiments The dimensions of the mold are 750 mm W 700 mm L 870 mm H The dominant parameter was varied within 10 of the proposed condition by the DOE to determine the optimal condition In order to examine the influence of core shift on the simulation of the injection molding process the results of the experiments are compared to those of the numerical analyses 3 Results and discussion 3 1 Results of injection molding analysis and DOE Fig 3 and Table 2 show the results of the injection molding analysis The flexible parts of the core were deformed in iden tical directions regardless of the combination of injection molding conditions as shown in Fig 3 Fig 3 and Table 2 show that the deformations of the F1 F5 and F6 parts of the core were greater than 0 1 mm and flexible parts of the core deformed symmetrically In addition it was noted that the shifts of the F2 and F3 parts are negligible in comparison with those of other parts From the results of the injection molding analysis the S N and contribution ratios were calculated for the F1 F5 and F6 parts of the core with relatively large core shifts Fig 4 and Table 3 show the results of the DOE In Fig 4 it can be seen that the S N ratios of the injection pressure the holding time the injection time and the initial mold tempera ture are maximized when their values are 30 MPa 1 6 seconds 4 4 seconds and 40 o C respectively The S N ratio of the in D G Ahn et al Journal of Mechanical Science and Technology 24 2010 145 148 147 Table 3 Pure contribution ratios of each injection molding parameter for different flexible parts Contribution ratio Flexible Parts Injection time Injection Pressure Holding time F1 4 1 56 5 15 8 F4 0 0 99 2 0 2 F6 3 3 73 3 6 3 Mean 2 5 76 3 7 4 a b Fig 4 Variation of signal to noise ratios according to the levels of injection molding parameters a S N ratios of injection pressure and holding time b S N ratios of initial mold temperature and injection time jection pressure also increases remarkably when the injection pressure decreases as shown in Fig 4 Table 3 shows that the mean value of the contribution ratio of the injection pressure is nearly 76 3 and that the contri bution ratio of the injection pressure is markedly higher than that of the other parameters From these results it was noted that the dominant parameter which mainly affects the core shift is the injection pressure The variation in S N ratio and the contribution ratio for the injection time and the initial mold temperature are negligible as shown in Fig 4 and Table 3 From these results it was noted that the injection time and the initial mold temperature hardly affect the core shift 3 2 Results of the experiments Using the results of the DOE the experimental conditions of injection time holding time and initial mold temperature were set at 1 6 seconds 4 4 seconds and 40 o C respectively The injection pressure was varied in the range of 27 32 MPa Fig 5 shows the results of the injection molding experi Fig 5 Molded product for different injection pressures a Injection pressure 30 MPa Condition proposed by the DOE b Injection pressure 32 MPa Optimal condition a b Fig 6 Comparison of the results of numerical analyses and those of the experiments a Thickness distribution of channels b Post deformation of the molded product ments The shortshot did not occur in all experimental condi tions as shown in Fig 5 However the warpages of the walls of the molded product occurred when the injection pressure was lower than 30 MPa as shown in Fig 5 a This results from the insufficient holding pressure The warpages of the product walls do not occur when the injection pressure is 32 MPa as shown in Fig 5 b From these results the optimal injection molding conditions of the tested plastic battery case with thin and deep walls were determined as an injection pres sure of 32 MPa an injection time of 1 6 seconds a holding 148 D G Ahn et al Journal of Mechanical Science and Technology 24 2010 145 148 time of 4 4 seconds and an initial mold temperature of 40 o C The results of the experiments were compared to those of the numerical analyses as shown in Fig 6 Fig 6 a shows that the difference in wall thickness between the analyses and the experiments is reduced from 0 15 mm 0 18 mm to 0 09 mm 0 07 mm when the core shift is considered in the nu merical analysis In addition it was noted that the thickness variation of the walls is properly predicted by the core shift analysis Fig 6 b shows that the core shift appreciably affects the post deformation pattern of the molded product and the numerical analysis accounting for the core shift can predict the post deformation of the product within 0 15 mm of computa tional accuracy The results of the numerical analyses show that the injection pressure is reduced from 50 2 MPa to 32 0 MPa when the core shift is considered This is due to in creased cavity volume induced by the elastic deformation of the core Based on the above results it is noted that injection molding analysis accounting for the core shift can properly simulate the injection molding process of the battery case with thin and deep walls 4 Conclusions The influence of injection molding parameters on the core shift in the molding of a plastic battery case with thin and deep walls was investigated using numerical analysis and the ex periment The elastic deformation of the core was considered to reflect core shift effects on the numerical analysis Through nu merical analysis and DOE it was shown that the injection pressure is the dominant process parameter affecting core shift and that the core shift decreases when the injection pressure decreases In addi tion it was noted that the injection time the holding time and the initial mold temperature hardly affect core shift It was demon strated through experiments that the molded product without war pages can be manufactured at an injection pressure of approxi mately 32 MPa Comparing the results of the numerical analyses with those of the experiments the optimal injection molding con ditions were obtained In addition it was shown that the core shift should be considered to accurately simulate the injection molding process of a plastic battery case with thin and deep walls References 1 R Spina Injection moulding of automotive component comparison between hot runner systems for a case study J Mater Process Technol 155 156 2004 1497 1504 2 K J Kim C W Sung Y N Baik Y H Lee D S Bae K H Kim and S T Won Hydroforming simulation of high strength steel cross members in an automotive rear subframe Int J Prec Eng Manuf 9 3 2008 55 58 3 K J Kim M H Rhee B I Choi C W Kim C W Sung C P Han K W Kang and S T Won Development of ap plication technique of aluminum sandwich sheets for auto motive hood Int J Prec Eng Manuf 10 4 2009 71 75 4 S C Chen R D Chien H H Tseng and J S Huang Re sponse of a sequential valve gate system used for thin wall injection molding J Appl Polym Sci 98 5 2005 1969 1977 5 A Bakharev Z Fan F Costa S Han X Jin and P Ken nedy Prediction of core shift effects using mold filing simu lation Proc of ANTEC2004 Plastics Chicago Illinois USA 2004 621 625 6 T A Shepard M O Connell K Powell and S Charwinsky Minimising coreshift in injection moulded container Plast Eng 52 2 1996 27 29 7 V Leo and C Cuvelliez The effect of the packing parame ters gate geometry and mold elasticity on the final dimen sions of a molded part Polym Eng Sci 36 15 1996 1961 1971 Dong Gyu Ahn received his B S degree in Production and Mechanical Engineer ing from Pusan National University Korea in 1992 He then received his M S and Ph D degrees from KAIST in 1994 and 2002 respectively Dr Ahn is currently a Professor at the Department of Mechanical Engineering at Chosun University in Gwang Ju Korea Dr Ahn s research interests include rapid prototyping and manufacturing lightweight sandwich panel laser material processing and molds and dies